4123 Fe-Co-O continuous composition spreads Fe-Co-O
Type: Sample show more
ObjectId: 15143 ExternalId: 4123
Created: 1/23/2019 3:34:02 PM by C04) Tobias Piotrowiak [tobias.piotrowiak@rub.de]
Updated: 11/11/2023 10:56:28 PM by C04) Tobias Piotrowiak [tobias.piotrowiak@rub.de]
Access: Public Sort Code (asc): 0
Description: Sample for Fe-Co-O continuous composition spreads (Fe-Co-O at Si + SiO2, ID=0004123) by Piotrowiak Tobias. Hot Deposition 3H at 700 °C; 80 sccm Ar; 40 sccm O2 10 min preheated at 700 °C before Deposition
[no file attached]
: Co-Fe-O
Associated Objects
-
4121 Chem. composition (Processed Data, 36682)
Raw DocumentChem. composition for Sample for Fe-Co-O continuous composition spreads (Fe-Co-O at Si + SiO2, ID=0004121, K3) by Piotrowiak Tobias. Fe 300 W; Co 150 W; Ar 80 sccm; O2 40 sccm; 3 mTorr; 3H Substrat ist streifen Si/SiO2 mit Kreuzchen Streifen zur Unte
000032916_00.00_36682.opj
-
4123 Photo (Raw Data, 36680)
PhotoPhoto for Sample for Fe-Co-O continuous composition spreads (Fe-Co-O at Si + SiO2, ID=0004123) by Piotrowiak Tobias. Hot Deposition 3H at 700 °C; 80 sccm Ar; 40 sccm O2 10 min preheated at 700 °C before Deposition (Raw Data, 36680)
000032914_00.00_36680.JPG
-
4116 synthesis (adhesion layer, 190116-K3-2, id=36523)
SynthesisSynthesis for Sample 4116 (adhesion layer, 190116-K3-2, K7, Fe-Co-O Continuous Composition Spread; Pt-Electrode (Ta-Adhesionlayer))
-
4116 synthesis (single material, 190116-K3-2, id=36589)
SynthesisSynthesis for Sample 4116 (single material, 190116-K3-2, K7, Fe-Co-O Continuous Composition Spread; Pt-Electrode (Ta-Adhesionlayer))
-
4122 synthesis (co deposition, 190123-K3-1, id=36669)
SynthesisSynthesis for Sample 4122 (co deposition, 190123-K3-1, K7, Fe-Co-O Continuous Composition Spread; Pt Electrode (Ta Adhesion) Hot Deposition 700 °C)
-
4123 SEM (image) (Raw Data, 45079)
SEM ImageSEM (image) for Sample for Fe-Co-O continuous composition spreads (Fe-Co-O at Si + SiO2, ID=0004123) by Piotrowiak Tobias. Hot Deposition 3H at 700 °C; 80 sccm Ar; 40 sccm O2 10 min preheated at 700 °C before Deposition (Raw Data, 45079)
000040795_00.00_45079.zip
Referenced Objects (Reverse Association)
-
ACS Combinatorial Science, 2020 (Piotrowiak)
PublicationT.H. Piotrowiak, X. Wang, L. Banko, S. Kumari, S. Sarker, A. Mehta, A. Ludwig. "High-Throughput Characterization of (FexCo1–x)3O4 Thin-Film Composition Spreads". ACS combinatorial science, 2020, 22(12), 804-812. DOI: 10.1021/acscombsci.0c00126
All properties (except table)
No properties found